HADALAN® Topcoat M 12P

Properties

• 2-component
• breathable
• matt surface
• lightfast
• solvent-free

Applications

• rigid reaction resin coatings
• Concrete and screed surfaces
• mastic asphalt indoors

Composition

• Polyurethane resin
• additives

Substrate

Suitable substrates

• Concrete and screed surfaces
• Mastic asphalt for indoor use

Properties/tests

• The substrate must be dry, load-bearing, clean, dust-free and free of adhesion-reducing residues, release agents, efflorescence and sintered coatings.
• There is a risk of condensation forming on the substrate surface in the event of significant temperature changes in conjunction with increased humidity. The substrate must be completely dry before starting the coating work. Otherwise, coating damp surfaces may result in peeling or irritation of the material surface.

Pretreatment

• For priming mineral, absorbent substrates, HADALAN Topcoat M 12P is diluted with 10 % water.

Processing

Mixing / Preparation / Processing

• Allow curing component to flow completely into the main component.
• Then repot into a clean container and intermix thoroughly again.

Processing

• HADALAN Topcoat M 12P is applied to the substrate with a mohair roller in a thin cross-coat.
• The specified consumption quantities must be observed. Excessive application quantities can lead to irritation of the material surface.

Drying / Hardening

• The surfaces can be carefully walked on after 4 hours, recoated after 6 hours and fully loaded after 5 days.

Cleaning the tools

• Clean all tools and equipment with water immediately after use.
• Hardened material can only be removed mechanically.

Notes

• Maintain a processing temperature of +5 °C to +30 °C.
• The substrate to be coated must be surface dry.
• High temperatures accelerate, low temperatures delay the solidification and curing process.
• The application distances for multi-layer coatings must be observed.
• Observe the consumption specifications. Increased layer thicknesses or puddle formation can lead to detachment or irritation of the coating surface.
• Do not use under permanent load from car tires.
• The substrate temperature must be at least 3 °C above the dew point temperature during application and curing.
• Irritation may occur on the surface in the event of uneven application thicknesses, draughts and large temperature differences.
• To keep traces of use as small as possible, we recommend fitting felt glides or similar under moving furniture parts such as tables and chairs and using floor protection mats under office chairs.