HADALAN® FGM035 57M

Properties

• easy to mix in
• easy to apply in combination with system resins
• low binder requirement
• low dust
• permeable to water
• homogeneous mixtures, the resin does not run off

Applications

• indoor and outdoor areas
• Balconies, terraces, arcades
• Levelling coats

Composition

• Mineral fillers

Substrate

Properties/tests

• The substrate must be firm, stable, free of frost, dust, dirt and other loose particles.
• Rising damp and residual moisture above 4 % must be excluded.
• The adhesive tensile strength should not be less than 1.5 N/mm², especially if the surface covering is expected to be subjected to high mechanical loads.

Pretreatment

• Non-load-bearing substrates must be prepared by milling, blasting, or similar methods.

Processing

Processing

• The respective resin is mixed as a primer and applied to the substrate. The mortar is applied to the fresh primer layer and compacted. If this is not possible, the primer layer is sprinkled with Quartz051 57M. After hardening, the sand that has not been incorporated must be swept away. With HADALAN EBG 13E only a "fresh in fresh" working method is possible. Scattering is not possible.
• Mix HADALAN MBH 12E or EBG 13E with a slow-running drill, repot and stir again briefly. Then add HADALAN FGM035 57M in the desired mixing ratio and mix with a powerful stirrer and large basket stirrer. The mixing process is only complete when the filler and the epoxy resin are homogeneously mixed together. Intermediate testing with a trowel helps to determine this point in time.
  
  Strengths in combination with HADALAN MBH 12E or HADALAN EG145 13E after 7 days
  10 % MV 1:10 GT resin:filler: 50 N/mm²
  5 % MV 1:20 GT resin:filler: 30 N/mm²
  4 % MV 1:25 GT resin:filler: 22.5 N/mm²
  
  Strengths in combination with HADALAN EBG 13E after 7 days
  5 % MV 1:20 GT resin:filler: 15 N/mm²
  4 % MV 1:25 GT resin:filler: 12.5 N/mm²
  
• Epoxy resins react exothermically. The mixed compounds should therefore be processed quickly. The processing time depends on the respective mixing ratio and the ambient temperatures. Depending on the conditions, a working time of 20 to 45 minutes is available.

Cleaning the tools

• When fresh, the tools can be cleaned with HADALAN^® MBH 12E using HADALAN^® EPV 38L and with HADALAN^® EBG 13E using water. In dry condition only mechanically.

Notes

• High temperatures accelerate, low temperatures delay the solidification and curing process.
• Always use whole bags, as the material can segregate when partially removed.
• For screeds on a separating layer or insulation, request advice from hahne application technology.
• The quantity of primer may vary greatly depending on the substrate and roughness.
• For subsequent coating systems, a pore-closing scratch coat must also be applied.
• The minimum thickness of the mortar is double the grain thickness.