HADALAN® FGM012 57M

Properties

• easy to mix in
• easy to process
• high mechanical and chemical resistance
• high chemical resistance
• low binder requirement
• universal use
• enables the production of liquid-tight fillings
• low dust

Applications

• Concrete and screed surfaces
• Industrial floors
• Balconies, terraces, arcades

Composition

• Mineral fillers
• Additives

Substrate

Properties/tests

• The substrate must be firm, stable, free of frost, dust, dirt and other loose particles.
• The residual moisture of the substrate must be < 4.0 CM%.
• Heavy loads lead to high pressure point loads during transportation. This must also be able to be absorbed by the underbody.
• The adhesive tensile strength should not be less than 1.5 N/mm², especially if the surface covering is expected to be subjected to high mechanical loads.

Pretreatment

• If there is a risk of moisture penetration from the back or water vapor diffusion, use the osmosis-resistant reaction resin HADALAN EG145 13E.
• Non-load-bearing substrates must be prepared by milling, blasting, or similar methods.

Processing

Processing

• As a primer, the respective resin is mixed and applied to the substrate. The mortar is applied to the fresh primer layer and compacted. If this is not possible, the primer layer is sprinkled with Quartz051 57M. After hardening, the sand that has not been incorporated must be swept away. With HADALAN EBG 13E only a "fresh in fresh" working method is possible. Scattering is not possible.
• Mix HADALAN MBH 12E or HADALAN EBG 13E with a slow-running drill, repot and stir again briefly. Then add HADALAN FGM012 57M in the desired mixing ratio and mix with a powerful stirrer and large basket stirrer. The mixing process is only complete when the filler and the epoxy resin are homogeneously mixed together. Checking in the meantime with a trowel helps to determine this point in time.
• Epoxy resins react exothermically. The mixed compounds should therefore be processed quickly. The processing time depends on the respective mixing ratio and the ambient temperatures. Depending on the conditions, a working time of 20 to 45 minutes is available.

Processing / Working time

• Depending on conditions, the working time is 20 to 45 minutes.

Cleaning the tools

• When fresh, the tools can be cleaned with HADALAN^® MBH 12E using HADALAN^® EPV 38L and with HADALAN^® EBG 13E using water. In dry condition only mechanically.

Notes

• Epoxy resins react exothermically. High temperatures accelerate, low temperatures delay the setting process.
• If there is a risk of moisture penetration or water vapor diffusion from the rear, the osmosis-stable resin HADALAN EG145 13E should always be used.
• When applying liquid-tight fillers, ensure that the mortar layer is sufficiently compacted. If necessary, a wetting test should be carried out to check for leaks.
• Optically related areas must be prepared with material from the same production batch to prevent colour differences.